Titebond Genuine Hide Glue
Franklin International · animal glue
Full cure (70°F / 50% RH)
24h
Min application temp
50°F
Clamp time
30 min
Open time
10 min
Estimate Cure Time
Common use-case guides
When this estimate may be unsafe
- - The joint, bead, pour, or repair is thicker than the product data sheet assumes.
- - The substrate is colder than the surrounding air, wet, oily, dusty, painted, or otherwise poorly prepared.
- - The repair will carry weight, resist water pressure, or be safety-critical before full cure.
Quick answers
How long does Titebond Genuine Hide Glue take to cure?
Titebond Genuine Hide Glue fully cures in 24 hours at standard laboratory conditions, usually 70°F / 21°C and 50% relative humidity. At colder temperatures or difficult humidity, cure time can increase significantly.
What is the minimum temperature to use Titebond Genuine Hide Glue?
The minimum application temperature for Titebond Genuine Hide Glue is 50°F (10°C). Applying below this threshold can prevent proper curing and cause the bond or seal to fail.
How long does Titebond Genuine Hide Glue take to cure in cold weather?
Cold temperatures significantly extend cure time. As a rule of thumb, every 18°F (10°C) below 70°F can roughly double cure time. Enter your actual temperature in the calculator for a product-specific estimate.
Does humidity affect Titebond Genuine Hide Glue cure time?
Yes. Titebond Genuine Hide Glue cures by water evaporation, so high humidity slows cure. Above 85% RH cure may fail entirely. Low humidity below 40% RH speeds drying but can cause the adhesive to dry before a proper bond forms. Optimal range is 40-60% RH.
How long do you need to clamp Titebond Genuine Hide Glue?
Titebond Genuine Hide Glue requires a minimum of 30 minutes of clamping at standard conditions. In cold or humid conditions, extend clamp time before moving the assembly.
What is the open time for Titebond Genuine Hide Glue?
Titebond Genuine Hide Glue has a working open time of 10 minutes at standard conditions. At higher temperatures open time may shorten; at lower temperatures cure may slow after assembly.